AlSi30Cu5 coating was prepared on the 6061 aluminum alloy by plasma spraying technology. The results showed that the phases were mainly α-Al, β-Si, and θ-Al2Cu. The size of the β-Si in the powder and coating was 3.51 μm and 2.06 μm respectively, that was, the β-Si in the coating was refined. The average hardness of the coating was 280 HV0.2, which was significantly higher that of the substrate (110 HV0.2). The wear rate of the coating was only 20 % of the substrate. Therefore, AlSi30Cu5 coating prepared by plasma spraying can provide effectively wear protection for the 6061 aluminum alloy. It is beneficial for promoting the further application and development of aluminum alloys.

Tribological behavior of graphene/DLC coatings after AO and UV irradiation in vacuum environment

Pub Date: 2023-12-20 DOI: https://doi.org/10.1016/j.matlet.2023.135800

[Jiadong Shi, Guozheng Ma, Guolu Li, Qingsong Yong, Weiling Guo, Zhiguo Xing, Haidou Wang]

Study of Wear and Corrosion Resistance of Cold Sprayed TC4 Coating on the Surface of Mg-Li Alloy

Pub Date: 2023-12-20 DOI: https://doi.org/10.1016/j.matlet.2023.135800

[Yongtao Bao, Binguo Fu, Yunlei Jiao, Tianshun Dong, Jingkun Li, Guolu Li]

Influence of the Reference Electrode on the Performance of Single-Electrode Triboelectric Nanogenerators and the Optimization Strategies

Pub Date: 2023-12-20 DOI: https://doi.org/10.1016/j.matlet.2023.135800

[Zetong Chen, Keren Dai, Jiaxiang Chen, Jingting Zhuo, Danna Zhao, Rui Ma, Xujing Zhang, Xubiao Li, Xiaofeng Wang, Guowei Yang, Fang Yi]