Medium-alloy ductile iron with a SiMo ferritic matrix has very good heat resistance. The addition of chromium and aluminum also increases this resistance. This article presents the impact of chromium and aluminum on the structure of SiMo cast iron, especially their impact on the deformation of the spherical graphite precipitates and the formation of M 6C and M 3C 2 carbide phases. These carbides are formed in a ferritic matrix or at the grain boundaries, resulting in increased hardness and a drastic reduction in impact strength. The article presents the influence of heat treatment on the material’s microstructure and resistance to abrasive wear. Chromium and aluminum additions can also indirectly reduce the abrasive wear resistance of SiMo cast iron. The presented research shows the possibility of doubling the abrasive wear resistance of SiMo cast iron. Abstract Medium-alloy ductile iron with a SiMo ferritic matrix has very good heat resistance. The addition of chromium and aluminum also increases this resistance. This article presents the impact of chromium and aluminum on the structure of SiMo cast iron, especially their impact on the deformation of the spherical graphite precipitates and the formation of M 6C and M 3C 2 carbide phases. These carbides are formed in a ferritic matrix or at the grain boundaries, resulting in increased hardness and a drastic reduction in impact strength. The article presents the influence of heat treatment on the material’s microstructure and resistance to abrasive wear. Chromium and aluminum additions can also indirectly reduce the abrasive wear resistance of SiMo cast iron. The presented research shows the possibility of doubling the abrasive wear resistance of SiMo cast iron. Keywords: ductile cast iron; SiMo cast iron; silicon addition; molybdenum addition; abrasive wear resistance; HV hardness