The layered double hydroxide (LDH) has been practically applied in the field of tribology and materials science due to its unique physicochemical properties, weak bonding, flexible structural composition, and adjustable interlayer space. In this work, a series of ultrathin and flexible composition of Ni-Fe LDH samples were prepared via a cost-effective room-temperature co-precipitation process. Then, they were mechanically dispersed into GTL base oil and their lubricating performance were tested by a four-ball tribometer. It is found that the variation of Ni-Fe ratio of Ni-Fe LDH has a great influence on the improvement of lubricating performance of GTL base oil. At the same concentration (0.3 mg/mL), the Ni-Fe LDH with Ni/Fe ratio of 6 was demonstrated to exhibit the best lubricating performance and the AFC, WSD, the wear volume, surface roughness and average wear scar depth decreased 51.3%, 30.8%, 78.4%, 6.7% and 50.0%, respectively. SEM-EDS and X-ray photoelectron spectra illustrated that the tribo-chemical film consisting of iron oxides and NiO with better mechanical properties formed and slowly replaced the physical film, which resists scuffing and protect solid surface from severe collisions.