Design/methodology/approach The NiTi–xAl2O3 coatings were fabricated on S355 steel by laser cladding, and their corrosive-wear and electrochemical performance were investigated using a wear tester and electrochemical workstation, respectively. Findings The wear rates of NiTi–5%Al2O3, –10%Al2O3 and –15%Al2O3 coatings are 82.33, 54.23 and 30.10 µm3 mm−1 N−1, respectively, showing that the wear resistance of NiTi–15%Al2O3 coating is the best. The wear mechanism is abrasive wear, which is attributed to the increase of coating hardness by the Al2O3 addition. The polarization resistance of NiTi–5%Al2O3, –10%Al2O3 and –15%Al2O3 coatings is 3,639, 5,125 and 10,024 O cm2, respectively, exhibiting that the NiTi–15% Al2O3 coating has the best corrosion resistance. Originality/value The roles of Al2O3 in the corrosive-wear and electrochemical performance of NiTi–xAl2O3 coating were revealed through the experimental investigation. Peer review The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-02-2024-0044/