In this study, multi-element nitride coatings composed of (Ti, Cr, Cu, Al, Si)N were synthesized on H13 tool steel using cathodic arc deposition (CAD) technology. The N 2/Ar flow ratio varied from 0 to 2 as the experimental parameter, and two targets, Ti-Cr-Cu and Al-Si alloys, were utilized simultaneously. The impact of the gas flow ratio on the coatings’ abrasion properties was investigated, focusing on aspects, such as chemical composition, adhesion, hardness, and wear behavior. The experimental findings indicate that the coated specimens with a nitrogen reaction exhibit superior hardness and abrasion resistance compared to those without nitrogen use. While the surface roughness of the specimens tends to increase slightly with a higher N2/Ar ratio, the coating demonstrates improved hardness, adhesion, and abrasion resistance performance. In summary, the wear-resistant characteristics of H13 tool steel can be significantly enhanced when applying a CAD-(Ti, Cr, Cu, Al, Si)N film with a flow ratio of N 2/Ar = 2. Abstract In this study, multi-element nitride coatings composed of (Ti, Cr, Cu, Al, Si)N were synthesized on H13 tool steel using cathodic arc deposition (CAD) technology. The N 2/Ar flow ratio varied from 0 to 2 as the experimental parameter, and two targets, Ti-Cr-Cu and Al-Si alloys, were utilized simultaneously. The impact of the gas flow ratio on the coatings’ abrasion properties was investigated, focusing on aspects, such as chemical composition, adhesion, hardness, and wear behavior. The experimental findings indicate that the coated specimens with a nitrogen reaction exhibit superior hardness and abrasion resistance compared to those without nitrogen use. While the surface roughness of the specimens tends to increase slightly with a higher N2/Ar ratio, the coating demonstrates improved hardness, adhesion, and abrasion resistance performance. In summary, the wear-resistant characteristics of H13 tool steel can be significantly enhanced when applying a CAD-(Ti, Cr, Cu, Al, Si)N film with a flow ratio of N 2/Ar = 2. Keywords: H13 tool steel; cathodic arc deposition; N2/Ar flow ratio; (Ti, Cr, Cu, Al, Si)N coating; adhesion; wear resistance
周老师: 13321314106
王老师: 17793132604
邮箱号码: lub@licp.cas.cn