Improving the wear resistance and corrosion resistance of 60Si2Mn steel is an important issue in agricultural machinery. A Rockit 606 coating layer may exhibit excellent performance in wear resistance and corrosion resistance. However, there are very a few public reports and articles involving the topic of a Rockit 606 laser cladding layer on a steel 60Si2Mn surface. It is of great importance to research Rockit 606 laser cladding layers. This work focuses on studying the microstructure and properties of Rockit 606 coating layers with different scanning speeds by disk laser cladding. Firstly, the laser cladding platform was designed and set up. Secondly, the laser cladding parameters were designed, and then the laser cladding experiment was conducted, and the Rockit 606 coating layers were obtained. And finally, the microstructure, phase distribution, corrosion resistance, surface hardness, and wear resistance of the coating layers were measured and analyzed. A scanning electron microscope (SEM), X-ray diffractometer (XRD), electrochemical workstation, and microhardness tester were used in this work. It was found that the microstructure Rockit 606 alloy coating consists of γ-Fe, V 8C 7, and Cr 7C 3. The microhardness of the Rockit 606 alloy coatings decreased with an increase in the scanning speed. When the scanning speed was 4 mm/s, the highest microhardness value reached 867.2 HV, which is about three times of that of the substrate. The average coefficients of friction (COFs) of the coatings decreased with an increase in the scanning speed, which led to the corresponding decrease of the wear rate. When the scanning speed was 4 mm/s, the wear behavior of the coating was mainly oxidative wear and a small amount of adhesive wear. The self-corrosion current density of the coatings prepared by laser cladding in a 3.5 wt.% NaCl solution is one order of magnitude lower than that of the substrate, indicating that the coatings have better corrosion resistance properties.