Al 1.8CrCuFeNi 2 high-entropy alloy coatings with different TiC contents were prepared using laser cladding. The effect of TiC on the microstructure, hardness and wear resistance of the coatings was investigated. It was found that the phase structure of the coating with 10 wt.% TiC was a single BCC phase with no other precipitated phase. When 20 wt.% TiC was added, the phase structure of the coating was a BCC phase and TiC phase. When the TiC content increased to 30 wt.%, more TiC-reinforcing phase was formed. With the increase in the TiC content, the hardness of the high-entropy alloy coating was enhanced and the wear loss clearly decreased, which was closely related to the change in the coating structure. The addition of TiC to high-entropy alloys plays the role of fine-grain strengthening and dispersion strengthening.