Seamless gas cylinders for diving exhibit excellent low-temperature impact performance, lightweight characteristics, and good corrosion resistance, making them widely applicable in underwater activities. However, during use, the peeling of paint or corrosion on the surface of these cylinders poses a significant threat to their safety. In this study, environmentally friendly arc ion plating technology was used to deposit TiBN, CrAlN, and nano-multilayer coatings of CrAlN/TiBN. The surface morphology, tribological properties, and corrosion resistance of these coatings were investigated. The results indicated that both CrAlN and CrAlN/TiBN coatings possess fewer droplets, pinholes, and pits, and the cross- of the CrAlN/TiBN coating exhibits a denser structure. The preferred orientation for TiBN was identified as TiB 2 (101), while that for CrAlN was Cr(Al)N (200), with the preferred orientation for CrAlN/TiBN being TiB 2 (101). The friction measurements revealed that the lowest coefficient was observed in the CrAlN/TiBN coating (0.489), followed by CrAlN (0.491) and then TiBN (0.642). Electrochemical tests conducted in artificial seawater demonstrated that the self-corrosion potential was highest for the CrAlN/TiBN coating, followed by CrAlN and lastly TiBN. The developed TiBN-based nano-multilayer coatings hold substantial application value in protecting seamless gas cylinders used in diving.